作者/來源：徐才福，殷為玉，李家偉，蔡永寧(中國五環(huán)工程有限公司，湖北 武漢 430223) 日期： 2012-08-16 點擊率：1909
摘 要：從腐蝕機理、水質和煤質影響、煤粉流動穩(wěn)定性等方面分析了殼牌煤氣化爐燒嘴罩發(fā)生漏水失效問題的原因；針對工程設計、施工管理和操作控制提出了改進措施和應對策略。
關鍵詞：殼牌煤氣化；燒嘴罩；腐蝕；磨蝕；過燒；應對措施
中圖分類號：TQ545 文獻標識碼：A 文章編號：1004-8901(2011)05-0023-06
Failure Reason Analysis and Repartee Repartee Strategy for Burner Muffle of Shell Coal Gasifier
XU Cai-fu，YIN Wei-yu，LI Jia-wei，CAI Yong-ning
(China Wuhuan Engineering Company Ltd.，Wuhan Hubei 430223 China)
Abstract：Author has analyzed the failure reason for water leakage occurred in Shell coal gasifier muffle from aspects of corrosion mechanism，effect of water quality and coal quality，stability for now of pulverized coal and so on；and has presented the improvement measures and repartee strategy in allusion to engineering design，construction management and operational control.
Key words：Shell coal gasifieation；burner muffle；corrosion；erosion；over-burning；repartee measares
到目前為止，采用殼牌粉煤加壓氣化技術的煤氣化裝置已有15套投入運行，還有3套正在試運行。為了達到裝置的長周期安全運行，殼牌公司、中石化公司、合肥通用機械研究所、業(yè)主及工程公司進行了大量研究和開發(fā)工作，提出不少改進措施，殼牌公司還相繼推出了第Ⅱ代、第Ⅲ代燒嘴罩。由于這些改進的重點是材料、燒嘴罩結構以及燒嘴與燒嘴罩之間的密封結構，盡管改進后燒嘴罩能適應較大的操作彈性，但燒嘴罩的穿孔漏水現(xiàn)象仍然時有發(fā)生。其原因是：由于熔融的渣沿突出的燒嘴罩端部分流的結果可能導致燒嘴罩下方膜式壁局部不能形成良好的渣層保護，膜式壁水冷管直接與火焰接觸，且由于熱流通量過大，引起局部過燒或形成高溫S和P的共晶體，產生高溫腐蝕和裂紋。因此燒嘴罩失效漏水問題依然是制約煤氣化裝置長周期運行的關鍵因素之一。鑒于此，筆者擬從失效機理入手，對工程設計、制造檢驗、操作管理等進行綜合分析，以期徹底解決燒嘴罩的失效問題。
1 燒嘴罩結構
燒嘴罩安裝在氣化爐反應室膜式壁處，與煤燒嘴和反....